Production of combustible fuels and carbon nanotubes from plastic wastes using an in

Scientific Reports volume 13, Article number: 9057 (2023) Cite this article

166 Accesses

1 Altmetric

Metrics details

This study performed in-situ microwave pyrolysis of plastic waste into hydrogen, liquid fuel and carbon nanotubes in the presence of Zeolite Socony Mobil ZSM-5 catalyst. In the presented microwave pyrolysis of plastics, activated carbon was used as a heat susceptor. The microwave power of 1 kW was employed to decompose high-density polyethylene (HDPE) and polypropylene (PP) wastes at moderate temperatures of 400–450 °C. The effect of plastic composition, catalyst loading and plastic type on liquid, gas and solid carbon products was quantified. This in-situ CMP reaction resulted in heavy hydrocarbons, hydrogen gas and carbon nanotubes as a solid residue. A relatively better hydrogen yield of 129.6 mmol/g as a green fuel was possible in this process. FTIR and gas chromatography analysis revealed that liquid product consisted of C13+ fraction hydrocarbons, such as alkanes, alkanes, and aromatics. TEM micrographs showed tubular-like structural morphology of the solid residue, which was identified as carbon nanotubes (CNTs) during X-ray diffraction analysis. The outer diameter of CNTs ranged from 30 to 93 nm from HDPE, 25–93 nm from PP and 30–54 nm for HDPE-PP mixure. The presented CMP process took just 2–4 min to completely pyrolyze the plastic feedstock into valuable products, leaving no polymeric residue.

Plastic products are ubiquitous in our daily lives. Because of their low cost, corrosion resistance, flexibility, durability, and lightweight, they are used in a variety of economic sectors, including residential, agricultural, automotive, commercial, medicine, packing materials, toys, demolition, and electrical equipment. High-density polyethylene (HDPE), polyethylene terephthalate (PET), low-density polyethylene (LDPE), polyvinyl chloride (PVC) and polypropylene (PP) were among the synthetic plastic polymers with the highest production rates over the past few years1,2,3. The applications of plastics are increasing with the increase in world population. Large-scale plastic production is raising several global concerns, including unsustainable production, environmental pollution and poor recycling processes or mechanisms2. Plastic waste management is essential for controlling environmental pollution at an acceptable level. Plastic polymers take decades to decompose and thus have an adverse impact on the environment. According to reports, waste plastic is the global 3rd largest producer of landfills. Due to a significant increase in plastic wrapping industries, the production of plastic has expanded from 1.5 million metric tons in 1950, to 359 million metric tons in 2018 and around 367 million metric tons in 2020. Approximately 250 million metric tons of plastic waste are dumped in landfills and discharged into the atmosphere directly each year. Approximately 10 million tons are openly released into the oceans and a predicted 9–13% annual waste plastic growth might be created by 20503. Waste plastics can discharge carcinogenic elements and other harmful compounds into landfills, contaminating groundwater. These toxic substances also reduce soil fertility. The marine ecology is also at risk from floating plastic debris in the ocean. Burning waste plastics produces dangerous emissions that are highly damaging to the environment when utilized as a direct energy source4,5.

Recycling plastic is challenging as removing many constraints of water pollution and other factors would be very expensive. Although recycling plastic would be able to minimize the amount of plastic waste, more consistent and maintainable methods are needed to convert the plastic waste to liquid oil, hydrogen gas fuel and CNTs5. The treatment of waste plastic has become a major problem, and pyrolysis is a tertiary chemical process that quickly transforms plastic waste into carbon and hydrogen fuel by thermally breaking down long-chain polymer molecules into smaller ones in an oxygen-free environment. The factors of pyrolysis products, such as temperature, catalyst type, residence time, pressure, reactor type, particle size, and fluidizing gas, all affect the quantity and quality of the product. It is possible to obtain desired valuable items by adjusting a number of parameters. For instance, the maximum liquid was produced during the pyrolysis of LDPE at 550 °C and PET at 520 °C. In order to generate desired products, the catalyst-plastic mixture, heat conversion, and reaction efficiency must all be carefully considered in the reactor design. The biomass and plastic waste are broken down using batch, continuous, or semi-batch reactors, conical spouted beds, fluidizing beds, and other similar geometries6.

Pyrolysis via microwave heating is a novel and promising technique for recycling waste plastic and biomass into fuel. Microwave-initiated pyrolysis process requires a dielectric substance to absorb microwaves. In the pyrolysis of plastics, caron back or activated carbon was used as a microwave susceptor, transforming microwave energy into thermal energy by changing the dipole alignment of polar molecules. The long-chain hydrocarbons of raw materials are broken into short-chain molecules through rapid microwave heating with high product selectivity7. A temperature in the range of 350–650 °C is required to disintegrate the polymer/biomass long-chain molecules into low molecular weight compounds in an oxygen-free environment because combustion of the product does not happen in an oxygen-free environment. Thermal decomposition of biomass produces combustible gases and charcoal. Most of the gases may be condensed into a combustible liquid known as pyrolysis oil, while some permanent gases like H2, CO, CO2 and light hydrocarbons are also observed in the process8. Microwave heating has many advantages as compared to conventional heating. This method ensures specific heating and higher efficiency of energy conversion. So, this technique is most appropriate for degrading materials containing biomass, brown coal, wood, and plastic waste9. Catalytic microwave pyrolysis also improves the polymer conversion rate, product distribution and yielding by reducing the process time and operating temperature. Microwave radiations target the material by heating the core of the material. Because of their acidic nature and porous structure, zeolites and metal oxide catalysts have been shown to be the most energetic catalysts. By modifying the characteristics of zeolites, suitable liquid and gaseous products can be obtained10.

A catalyst is required for catalytic pyrolysis to accelerate the reaction and convert plastic wastes into liquid oil at relatively low temperatures. Various types of catalysts are used, such as Fluid Catalytic Cracking (FCC), Zeolite Socony Mobil-5 (HZSM-5, ZSM-5), Natural Zeolite, Cu-Al2O3, and Red Mud. Chen et al.11 produced a magnetic catalyst from diaper waste to catalyze the reaction to produce biodiesel. They reported that this catalyst is highly efficient, environmentally friendly and low-cost compared to other catalysts. Wang et al.12 derived porous carbon from potassium citrate for CO2 capture and dye adsorption applications. In pyrolysis, the catalyst drives the rate of cracking, which results in a rapid increase in gas production with decreased liquid oil. In this study, the reactivity of zeolite catalysts on feedstock in MAP was studied. A catalytic fixed bed reactor was utilized in the ex-situ procedure to increase the activity of the catalyst. The microwave-assisted pyrolysis of Douglas fir in the presence of ZSM-5 has produced aromatic and phenol- range hydrocarbons13. Microwave pyrolysis of HDPE using ZSM-5 catalyst has produced 47.4% yield of liquid and 24.5% of waxes at 560 °C14,15. In response to these findings, in-situ microwave pyrolysis of polyethylene and polypropylene into hydrogen, liquid fuel, and carbon nanotubes was carried out in the presence of a Zeolite Socony Mobil ZSM-5 catalyst.

The pure and mixed forms of HDPE and PP wastes were used in the microwave pyrolysis experiments. The plastic feedstock was recovered from household plastic bottles, shampoo bottles and food containers. The main characteristics and composition of plastics and their mixture are given in Table 1. The plastics were washed, dried and chopped into 5 mm pieces and fed into the pyrolytic reactor, as shown schematically in Fig. 1a. ZSM-5 catalyst of analytical grade was purchased from a chemical store and used to convert plastic waste hydrocarbons into diesel and gasoline range hydrocarbons and syngas. ZSM-5 is a microporous, 3D synthetic zeolite that contains alumina (Al) and silica (Si), with silica content notably higher than alumina. The chemical composition of the catalyst is: Silicon Oxide-33%, Aluminum Oxide-28%, Sodium Oxide-17% and water-22%. With Si/Al ratio of 40, the catalyst had a pore diameter of 5 Å, surface area of 397 m2/g and pore volume of 0.178 cm3/g. The catalyst was activated by calcining it at 500 \(^\circ{\rm C}\) for 2 h. The activated carbon worked as a heat susceptor to initiate the pyrolysis process by absorbing microwave energy in the presence of ZSM-5 catalyst. The heat susceptor converted microwave radiations into thermal waves, decomposing the plastic waste into high-value hydrocarbons, as explained in Fig. 1b.

(a) Schematic of pyrolysis setup: (1) microwave reactor; (2) waveguide; (3) microwaves; (4) ceramic fibred block; (5) pyrolysis reactor; (6) nitrogen gas inlet; (7) thermometer; (8) Liebig condensers; (9) oil collecting flasks; (10) gas sampling; (11) cold traps; (12) connecting tubes. (b) Mechanism involved in destruction of plastic into liquid fuel and gaseous products through catalytic microwave pyrolysis.

The catalytic microwave pyrolysis setup was built up by modifying the household microwave oven into a microwave pyrolysis reactor working at 1 kW power, with temperature ranges from 400 to 450 °C , provided microwaves of frequency 2450 MHz from the waveguide shown in Fig. 1a. There were two thermocouples: one for monitoring the vapor temperature and 2nd for monitoring the pyrolysis process temperature. The later thermocouple was in contact with the feedstock. A microwave source, consisting of magnetons, was operated at 100 °C to produce microwaves. Magneton functioning at 100 °C refers to the magnetron temperature when it generates microwaves to heat the feedstock in the temperature range of 400–450 °C. The apparatus temperature is 100 °C, while the microwave process temperature is 400–450 °C. The focused microwaves pyrolyze the waste plastic by changing the dipole alignment of polar molecules. The nitrogen was added to the reactor cavity at a flowrate of 1.5 L/min to create the working environment for the pyrolysis process. The ceramic fibred block was placed below the pyrolytic reactor to minimize the heating loss. Condensers, cold traps, oil collecting flasks and gas analyzer were used to condense and maintain the pyrolytic vapors flow and separate them into liquid and gas fuels. The liquid oil was collected into flasks and gas was analyzed using a gas analyzer.

In this catalytic microwave pyrolysis process, 50 g of HDPE and PP were chopped into 5 mm pieces. The plastic feedstock, ZSM-5 catalyst and activated carbon with a ratio of 10:1 was directly faded into the pyrolytic reactor. The mixture of plastic wastes (HDPE and PP), ZSM-5 catalyst and activated carbon reacted and produced the pyrolytic vapors, which passed through the condensation apparatus, and separated into valuable products. A cold trap consisted of two condensers and a water-cooling pump to cool and control the flow of liquid oil. The solid residue obtained at the end of the process was collected from the reactor for further analysis. The solid residue at the end of the pyrolysis process was identified as multi-walled CNTs. The yield of liquid oil products was calculated by weighing the collecting flasks after the pyrolysis process. The residue yield was estimated by comparing the weights of the pyrolysis pot at the start and end of the pyrolysis process.

The interaction of microwaves with material and conversion of microwaves into heat energy for decomposition of plastic waste into useful products is illustrated schematically in Fig. 2. In the case of microwave pyrolysis, a dielectric material is used as a microwave absorber or susceptor. We used activated carbon as a dielectric substance that absorbed the microwaves and converted them into heat energy. In an interaction between microwave radiations and dielectric material, the electric field directly interacts with the charged particles (e-) of the materials to generate heat, which causes the dislocation of charged particles from their equilibrium positions4. It involves two mechanisms: dipole polarization and dipole rotation. In dipole polarization, the permanent or induced dipoles of the molecules tend to align in the direction of the oscillating electric field.

Mechanism of interaction of microwave radiations with dielectric for pyrolysis of waste plastic in the presence of Na/ZSM-5 catalyst.

In dipole rotation, the polar molecules rotate back and forth continuously to align the dipole in a fluctuating electric field. The reorientation between rotating molecules in both mechanisms results in friction, which causes heat generation5. The generated heat is highly selective and rapidly interacts with plastic waste when sodium zeolite is used as a catalyst. The long-chain hydrocarbons of plastic were cracked and converted into shorter-chain hydrocarbons of aromatics or alkenes (wax) with the evolution of hydrogen gas as a fuel and solid carbon residue.

Figure 3a provides a comparison of product yield obtained via thermal and microwave deconstruction of plastic waste. The microwave pyrolysis was performed in an oxygen-free environment in the temperature range of 4000–450 °C. On the other hand, thermal pyrolysis process takes several hours to complete even at higher temperatures. In the microwave pyrolysis process, high liquid and gas yields were obtained within 24 min at relatively lower temperatures (400–450 °C) in the absence of oxygen16,17,18,19. Compared with the thermal decomposition of plastic waste, the yield of solid char also decreased in the microwave pyrolysis process. About 85–95% of feedstock was successfully converted into valuable products. In the microwave pyrolysis process. The desirable products can be obtained by manipulating the pyrolysis parameters i.e. retention time, catalyst type, temperature, and feedstock-to-catalyst ratio18,19. Figure 3b demonstrated the effect of plastic-type on the product yield at 450 °C temperature in the presence of Na/ZSM-5 catalyst. The graph illustrated that the yield of liquid oil, obtained from HDPE, PP and mixture (HDPE-PP), was about 56%, 48% and 42%, respectively. Similarly, the gas that evolved from these plastic wastes was about 24%, 40% and 42%, respectively. The char residue obtained from HDPE and mixture was maximum as compared to PP20. The gas contained a high concentration of hydrogen and some concentration of other gases like methane, carbon monoxide and carbon dioxide. Various types of catalysts are used to improve the composition and distribution of pyrolysis products, such as gas fuel and liquid oil. The presence of catalysts affects the pyrolytic temperature as well. The catalyst accelerates the reaction, transforming waste plastic into valuable products21.

(a) A comparison on product yield obtained via thermal and microwave pyrolysis methods, (b) effect of plastic type on product yield in the presence of Na/ZSM-5 catalyst at 450 \(^\circ{\rm C}\), (c) time-on-stream evaluation of product yield from HDPE, (d) PP, and (e) HDPE-PP.

Figure 3c–e shows the product yield distribution and composition obtained from HDPE, PP and mixture (HDPE-PP) over time. To study the effect of catalyst on product distribution, feedstock in 10:1 ratio with catalyst was pyrolyzed in a microwave reactor at 450 °C temperature. The time-on-stream evolution of product distribution in 4 min was divided into 3 steps during the process. In 1st step, the yield of gas (vapors) produced from the process increased from 80 to 88%, solid residue from 10 to 15%, while a negligible amount of liquid oil was observed. In the 2nd step, the gas yield decreased from 88 to 50%, char residue (waxes) increased from 30 to 40%, and liquid oil slightly increased. In 3rd step, the liquid oil, and gas yields approached to 48% and 24%, respectively and solid char reduced to 15% in contrast to other stages of time-on-stream evaluation on product yield14,22.

Table 2 shows the influence of different pyrolytic parameters on the yield of liquid oil, gas and solid residue. HDPE undergoes 80% conversion into valuable products, while the conversion of PP and HDPE-PP mixture was 88% and 84%, respectively. The conversion of feedstock into useful products was estimated using Eq. (1). Similarly, liquid, gas, char yield, and energy reconvey in the form of liquid oil were calculated using Eqs. (2–7)23,24,25.

In this equation, M is mass of plastic (g), M1 is liquid mass (g), M2 is solid residue (g), V1 is the volume of liquid oil in ml, and \(\rho\) is the density of liquid oil (g/cm3).

The HHV of a fuel is the amount of energy released by a specific quantity of feedstock at the initial temperature once it is decomposed. The HHV of oil from the pyrolysis of plastic waste was calculated depending on elemental analysis by using the following equation14:

In this equation, O = Oxygen, H = Hydrogen, C = Carbon, S = Sulphur and N = Nitrogen.

Figure 4a reports volume percentage of H2, CH3, CO, and CO2 evolved from catalytic microwave pyrolysis of HDPE, PP, and their mixture (HDPE-PP). The H2, CH3, CO composition of HDPE, PP, and HDPE-PP was measured about 78–81%, 6–8%, 7–8%, respectively. Figure 4b demonstrates the hydrogen gas yield (mmol/g) distribution evolved from HDPE, PP, and its mixture over several successive cycles in each experiment. In HDPE decomposition, the highest hydrogen gas evolved in 3rd cycle in contrast to other cycles, typically between 91.7 and 126.9 mmol/g. In PP pyrolysis, the maximum amount of hydrogen gas was observed in 4th cycle in the range of 66.9–101.1 mmol/g. In microwave pyrolysis of HDPE-PP, the maximum hydrogen gas composition was detected in 3rd cycle in the range of 88.8–107.6 mmol/g. The highest hydrogen gas efficiency was measured during microwave pyrolysis of HDPE, PP, and HDPE-PP at 450 °C (Fig. 4c). The maximum hydrogen gas that evolved from HDPE during the pyrolysis process was 126.9 mmol/g, while in PP, and HDPE-PP pyrolysis, the evolved gas was 101.1 mmol/g and 107.6 mmol/g, respectively.

(a) Different gas compositions of H2, CH3, CO, and CO2 over plastic type, (b) hydrogen gas efficiency (mmol/g) for each cycle of experiment for different plastic wastes, and (c) highest gas yield efficiency in different plastic wastes at 450 °C.

The probe of a gas analyzer was injected into the microwave reactor to check the gas efficiency after every 30 s of the pyrolysis process26. The gas analyzer was used to calculate the volume and composition of gases, from which the masses of each gas can be calculated. The following Eqs. (8–10) calculate the yield of obtained gas. The H2 yield is calculated by dividing the number of moles of H2 by the total mass of plastic utilized. The efficiency of H2 was determined by dividing the mass of H2 present in all gases by the theoretical amount of H2 contained in plastic27.

where mp is plastic waste mass, mg is gas amount, mH2 is the moles of hydrogen, mgH is the total hydrogen mass present in the gaseous product and mTh is the theoretical hydrogen mass present in plastic. Table 3 demonstrates the gas composition (vol%) evolved from microwave pyrolysis of HDPE, PP, and mixture (HDPE-PP) with feedstock to catalyst ratio of 10:1 at 450 °C. The gas evolved from this process mainly contained a high value of H2, and some amount of CH3, CO, and CO2 and other impurities.

TGA is an analytical technique used to determine the thermal stability of a material as well as the amount of volatile chemicals present in the sample under investigation. Figure 5a shows TGA curves of HDPE, PP, and HDPE-PP feedstocks in the range of 100–800 °C. Because the plastic material structure lacks inherent water, thermal degradation occurs at higher temperatures and took less time28. As the temperature of the plastic mixture rises from 100 to 300 °C, the material first melts and moisture present in the plastic is dried, but a further increase in temperature from 320 to 540 °C causes the chemical bonds to break. Due to the similarity of the chemical linkages in the molecular structures of HPDE and PP, the degradation of HDPE-PP revealed only one peak in the temperature range of 300–450 °C.

(a) Thermogravimetric curves of different waste plastics, (b) FTIR of oil obtained from microwave pyrolysis of different plastic wastes, and (c) X-ray diffraction spectra of solid residue in the form of CNTs.

Instead of burning, the active microwave pyrolysis process occurs when the sample is heated under a nitrogen environment in the absence of air. As a result, TGA testing environment would be exactly similar to that of a pyrolysis reactor. Thermal degradation begins with an increasing slope for all samples. The slope of the graph diminishes after passing through an extreme and ultimately becomes horizontal, where char production occurs29. The TGA profiles were produced in the temperature range of 100–800 °C. It has been discovered that mixed waste plastic degrades faster than separate plastics, resulting in a synergistic effect. The plastic degradation started after 300 °C and no degradation or weight loss was observed after 600 °C. Any changes in weight at temperatures below 300 °C, also called initial temperature, were due to removal of moisture content or drying of the sample. Volatile material was found in the range of 300 to 600 °C. The residue remains unchanged after 600 °C.

The CNTs from PP waste were made up of multiple components with degradation temperatures range of 400–550 °C. Each polymer showed a single phase breakdown into CNTs as represented by a single peak. The TGA curve showed that HDPE started degrading at temperatures near 350 °C and finally degraded at a high temperature of 600 °C. HDPE has a highly linear structure. PP is made up of repeated units that have methyl groups on a core carbon chain as a side chain. As a result, the PP degradation temperature was lower than the HDPE degradation temperature30. The TGA curve for a mixture of HDPE and PP showed a high linear degradation curve. Table 4 gives the initial weight loss and oxidation temperature of different plastic wastes pyrolyzed via the microwave pyrolysis method.

FTIR spectra and chemical compounds with functional groups of hydrocarbons in oil obtained from the catalytic pyrolysis of HDPE, PP and HDPE-PP are given in Fig. 5b. FTIR spectra showed typically similar results for oils obtained from different plastic wastes with slightly varying peak intensities. The classification of chemical compounds and functional groups of oil products are given in Table 5. The FTIR peaks, ranging from 3000 to 2840 cm-1, revealed high intensities corresponding to asymmetric C–H stretching bands. These bands revealed the presence of alkanes in the hydrocarbons of oils. The FTIR peaks in 1683–1286 cm-1 range represent alkenes or aromatic rings C–O and C–H stretching bending vibration in the sample. The peaks in the range of 970–897 cm-1 revealed C–H bending vibration and fingerprints of alkenes. The absorption peaks observed in the 800–690 cm-1 region showed single-ring aromatic compounds. These peaks confirmed C–H out-of-plane bending in the compounds of oil31,32. The obtained oils were rich in alkanes and alkenes like aliphatic hydrocarbons. They also contained a small amount of single-ring aromatic hydrocarbons, ketones, and aldehydes. FTIR spectra of liquid fuel were also compared with diesel and heavy gasoline range hydrocarbons. The high-intensity peaks of aliphatic compounds were similar to diesel fuel, which had the potential to convert plastic wastes through microwave pyrolysis into valuable heavy liquid fuel (waxes) that would be upgraded by hydrogenation method into light-weight diesel fuel33,34.

XRD patterns of CNTs product of microwave pyrolysis of HDPE, PP and HDPE-PP feedstocks are reported in Fig. 5c. XRD peaks at 2\(\theta\) of 26.1\(^\circ\), 39.3\(^\circ\), and 44.4\(^\circ\) were assigned to (002), (100), and (101) diffraction planes, respectively. A sharp characteristic peak of (002) plane appeared in all samples, indicating the graphite structure of CNTs. The intensity and FWHM of this peak are interlinked with interplanar d-spacing and lattice parameters of the material35,36. The interplanar space (d002) increases with the process temperature. The large value of FWHM indicated that CNTs have more defects, resonance, and distortion. Relative intensities of diffraction peaks deduced the position of the atoms within a unit cell compared with the most intense peak (002) of XRD pattern37,38. The interplanar space (d002) of intense peak (002) indicated the maximum microwave catalytic conversation of plastic into CNTs compared with the other two peaks39,40. The relative intensities of planes of (120) and (202) were compared with sharp peak (002) intensity, which deduced the position of the atom in a unit cell of hexagonal crystal structure of CNTs. The low interplanar d-spacing (0.34) showed a high crystalline structure of CNTs. The crystalline size, relative intensity, and other parameters depending on XRD were calculated using Bragg's law and the Scherrer equation. The findings of XRD analysis are reported in Table 6. The broadening of diffraction peaks in XRD patterns was analyzed to calculate the in-plane crystallite size of CNTs. The curved wall of CNTs affects their diffraction patterns and, consequently the crystallite size. The Scherrer equation for relating crystal edge length to peak breadth was used in these calculations:

where θ in this equation is a diffraction angle, λ wavelength of the diffraction, K is a Scherrer constant, and Δ(2θ) is line broadening due to crystallite size. Since scattering angles were sufficiently small, the approximation \(cos\theta \approx 1\) was used in these calculations. The crystalline size was calculated using (002) and (110) peaks. The interplanar spacing (d002) was calculated using Bragg's law:

where \(\lambda\) is the wavelength X-rays, d(Å) is interplanar spacing.

STEM images of the solid product of catalytic pyrolysis of HDPE, PP and HDPE-PP are shown in Fig. 6. Since STEM images are not as clear as TEM images, these images provide a rough understanding of the internal structure of the nanotubes. The STEM images revealed multi-walled structures of CNT product. All CNTs samples contained some catalyst particles and residual impurities. Significant growth of CNTs during microwaves assisted catalytic cracking of pure and mixed plastic wastes over ZSM-5 catalyst. A typical hexagonal morphology with a clinoptilolite phase of ZSM-5 catalyst and needle-like morphology with a mineralogical phase of CNTs was observed. These CNTs correspond to (002) plane, showing better crystallinity of tube structure41,42. The outer diameter of CNTs ranged from 30 to 93 nm from HDPE, 25 nm to 93 nm from PP and 30 nm to 54 nm for HDPE-PP mixture.

STEM images of CNTs produced during pyrolysis of HDPE (a), PP (b), and HDPE-PP (c).

The mixed waste produced the narrowest diameter of CNTs. The structures were also in more developed form with uniform morphology as compared to pure HDPE and PP. The catalyst particles are also smaller and lower in number in CNT structures from mixed plastic waste. Since large number of branched chains in PP facilitate fast decomposition of pure PP molecules, it is challenging to grow well-structured CNTs due to fast cracking of chains in PP. On the other hand, decomposition of pure HDPE molecules is assumed to be slower than PP. HDPE contains unbranched carbon chains, which make it difficult to decompose at a fast rate. The decomposition of pure HDPE also results in a more complex residue than pure PP. Therefore, HDPE-produced CNTs pose more defects and rugged surface morphology due to low degree of graphitization. Having a good mix of unbranched and branched carbon chains, HDPE-PP mixture undergoes decomposition at moderate rates allowing the formation of well-structured nanotubes. The CNT structures, produced with pure plastic wastes, contained a large number of agglomerated catalyst particles and amorphous carbon43. The entrapped impurities and catalyst particles can clearly be seen STEM images in Fig. 6. Wang et al.44 conducted catalytic pyrolysis of plastic waste for the production of valuable carbon in an effort to convert waste materials into and energy and valuable materials. They tested Ni/cordierite, Fe/cordierite and Ni-Mg/cordierite catalysts to pyrolyze polypropylene plastic. The Ni/cordierite catalyst results in the highest filamentous carbon yield of 93%. The strong metal-support interaction inside the Ni-Mg-based catalyst inhibited CNT growth, resulting in CNTs that were shorter in length and bigger in diameter (about 30–50 nm). Most of the tubes were found in irregular cylindrical shapes.

The chemical composition and main components of liquid products of microwave pyrolysis of HDPE, PP and HDPE-PP were identified using gas chromatography analysis. The liquid product was initially dissolved in methanol to determine its chemical composition. A typical GC–MS profile of the composition of the liquid product is given in Fig. 7. This typical time-based GC profile illustrates the time-dependent composition of the liquid product. Table 7 lists the chemical compounds in the liquid product with their chemical formula, chemical weight and concentration. It is illustrated that amount of aromatic hydrocarbons decreased from 53.7 to 0.3% and normal aliphatic hydrocarbons increased from 3.1 to 24.8% after 30 min of run time. In line with this, the gasoline fractions (C5–C12) decreased from 84.1 to 52.9%45. Table 7 clearly illustrates changes in yield of wax, n-alkene content, aromatic content and gasoline fractions at the end of the processing. Alkanes account for nearly 56.31% of these chemicals, alkenes for 29.71%, and alcohol accounts for 13.98%. The cracking of the precursor's C–C bond causes the production of alkanes. Similarly, alkene production is attributed to the breakdown of C–H and C–C bonds. It contained C6–C12 and heavy gasoline-range hydrocarbons of C13+ fractions46.

A typical GC–MS profile of liquid product obtained during microwave pyrolysis of plastic waste.

In terms of chemical makeup, the products obtained using microwave pyrolysis were remarkably similar to those obtained through thermal pyrolysis. During microwave pyrolysis of plastic, a reduction in the catalytic activity of ZSM-5 was noticed; specifically, the catalytic activity was judged lowered after 30 min. Catalytic pyrolysis gave a higher liquid yield of 48.9% compared to 40.2% from thermal pyrolysis. Similarly, very little wax (1.2%) was found compared to 15.7% wax from thermal pyrolysis47,48. The aromatic percentage of the liquid product was 45%, which was significantly higher than the aromatic content of thermal pyrolysis, which was 18.6%. Similarly, microwave pyrolysis produced better yield of isomerized aliphatic (24.6%) compared to 10.4% from thermal pyrolysis and C5–C12 gasoline fractions of 73.5% compared to 54.3% from thermal pyrolysis. However, n-alkene content was much lower from microwave pyrolysis than thermal pyrolysis (12.8 vs. 44.0%). This is consistent with the catalyst's well-known catalytic activity in cracking, aromatization and isomerization due to its balanced mix of acidity, microporous structure, and shape selectivity49,50. The graphical representation of the area concentration of hydrocarbons is shown in Fig. 8.

Graphical representation of components of oil from microwave pyrolysis of plastic: (a) HDPE, (b) PP, and (c) HDPE-PP.

Polypropylene and high-density polyethylene were decomposed through in-situ catalytic Microwave pyrolysis using a ZSM-5 catalyst. The activated carbon was employed to absorb microwaves and then release heat to plastic for the pyrolysis into liquid and solid products. This process aimed to synthesize gasoline-range liquid fuel, hydrogen gas, and solid residue as CNTs. The highest efficiency of hydrogen gas (126.9 mmol/g) was analyzed through gas analyzer. The TGA analysis of plastic waste HDPE, PP and mixture of HDPE and PP showed the thermal degradation of plastic into solid residue at temperatures ranging from 3400 to 650 °C. The outer diameter of CNTs ranged from 30 to 93 nm from HDPE, 25 nm to 93 nm from PP and 30 nm to 54 nm for HDPE-PP mixure. The mixed waste produced the narrowest diameter CNTs. The structures were also more developed with uniform morphology than pure HDPE and PP. The catalyst particles are also smaller and lower in number in CNT structures from mixed plastic waste. FTIR profiles of liquid products of pyrolysis of PP, HDPE, and mixture of PP and HDPE revealed that liquid oil contained hydrocarbons with C–H bending of alkanes, alkenes, and alkyl group respectively. The gas chromatography analysis of liquid fuel revealed that oil fuel contained gasoline range hydrocarbon range of C6–C12 and heavy hydrocarbon C13+ fractions. The X-ray diffraction analysis of CNTs synthesized from plastic waste showed that at (002) diffraction peak, the high intensity and less FWHM value of CNTs have more hexagonal crystalline structure as compared to other diffraction peaks and intensities. The STEM analysis of CNTs illustrated tubular-like structural morphologies of carbon nanotubes synthesized from pyrolyzed waste plastic.

The data reported in this paper is available from the corresponding authors on a reasonable request.

Papari, S., Bamdad, H. & Berruti, F. Pyrolytic conversion of plastic waste to value-added products and fuels: A review. Materials 14(10), 2586 (2021).

Article ADS CAS PubMed PubMed Central Google Scholar

Gong, J., Chen, X. & Tang, T. Recent progress in controlled carbonization of (waste) polymers. Prog. Polym. Sci. 94, 1–32 (2019).

Article CAS Google Scholar

Ramzan, F. et al. Single step microwaves assisted catalytic conversion of plastic waste into valuable fuel and carbon nanotubes. Thermochim. Acta 715, 179294 (2022).

Article CAS Google Scholar

Jia, M. et al. Upcycling waste polyethylene into carbon nanomaterial via a carbon-grown-on-carbon strategy. Macromol. Rapid Commun. 43, 2100835 (2022).

Article CAS Google Scholar

Elordi, G. et al. Catalytic pyrolysis of HDPE in continuous mode over zeolite catalysts in a conical spouted bed reactor. J. Anal. Appl. Pyrol. 85(1–2), 345–351 (2009).

Article CAS Google Scholar

Miandad, R., Barakat, M. A., Aburiazaiza, A. S., Rehan, M. & Nizami, A. S. Catalytic pyrolysis of plastic waste: A review. Process Saf. Environ. Prot. 102, 822–838 (2016).

Article CAS Google Scholar

Zaker, A., Chen, Z., Wang, X. & Zhang, Q. Microwave-assisted pyrolysis of sewage sludge: A review. Fuel Process. Technol. 187, 84–104 (2019).

Article CAS Google Scholar

Miandad, R. et al. Plastic waste to liquid oil through catalytic pyrolysis using natural and synthetic zeolite catalysts. Waste Manage. 69, 66–78 (2017).

Article CAS Google Scholar

Undri, A., Meini, S., Rosi, L., Frediani, M. & Frediani, P. Microwave pyrolysis of polymeric materials: Waste tires treatment and characterization of the value-added products. J. Anal. Appl. Pyrol. 103, 149–158 (2013).

Article CAS Google Scholar

Arshad, H., Sulaiman, S. A., Hussain, Z., Naz, Y., & Basrawi, F. (2017). Microwave assisted pyrolysis of plastic waste for production of fuels: A review. In MATEC Web of conferences (Vol. 131, p. 02005). EDP Sciences.

Chen, H., Xia, W. & Wang, S. Biodiesel production from waste cooking oil using a waste diaper derived heterogeneous magnetic catalyst. Braz. J. Chem. Eng. https://doi.org/10.1007/s43153-022-00257-z (2022).

Article Google Scholar

Wang, S. et al. Potassium citrate-derived porous carbon with high CO2 capture and Congo red adsorption performance. Environ. Sci. Eur. 35, 1–13 (2023).

Article Google Scholar

Panda, A. K., Singh, R. K. & Mishra, D. K. Thermolysis of waste plastics to liquid fuel: A suitable method for plastic waste management and manufacture of value added products—a world prospective. Renew. Sustain. Energy Rev. 14(1), 233–248 (2010).

Article CAS Google Scholar

Zhou, N. et al. Catalytic pyrolysis of plastic wastes in a continuous microwave assisted pyrolysis system for fuel production. Chem. Eng. J. 418, 129412 (2021).

Article CAS Google Scholar

Li, K. et al. Fe-, Ti-, Zr-and Al-pillared clays for efficient catalytic pyrolysis of mixed plastics. Chem. Eng. J. 317, 800–809 (2017).

Article CAS Google Scholar

Russell, A. D., Antreou, E. I., Lam, S. S., Ludlow-Palafox, C. & Chase, H. A. Microwave-assisted pyrolysis of HDPE using an activated carbon bed. RSC Adv. 2(17), 6756–6760 (2012).

Article ADS CAS Google Scholar

Mahari, W. A. W. et al. Production of value-added liquid fuel via microwave co-pyrolysis of used frying oil and plastic waste. Energy 162, 309–317 (2018).

Article Google Scholar

Mokhtar, N. M., Omar, R. & Idris, A. Microwave pyrolysis for conversion of materials to energy: A brief review. Energy Sources Part A Recovery Utilization Environ. Effects 34(22), 2104–2122 (2012).

Article CAS Google Scholar

Jie, X. et al. Microwave-initiated catalytic deconstruction of plastic waste into hydrogen and high-value carbons. Nat. Catal. 3(11), 902–912 (2020).

Article CAS Google Scholar

Yu, Y., Yu, J., Sun, B. & Yan, Z. Influence of catalyst types on the microwave-induced pyrolysis of sewage sludge. J. Anal. Appl. Pyrol. 106, 86–91 (2014).

Article CAS Google Scholar

Aboulkas, A. & El Bouadili, A. Thermal degradation behaviors of polyethylene and polypropylene. Part I: Pyrolysis kinetics and mechanisms. Energy Convers. Manag. 51(7), 1363–1369 (2010).

Article CAS Google Scholar

Dogu, O. et al. The chemistry of chemical recycling of solid plastic waste via pyrolysis and gasification: State-of-the-art, challenges, and future directions. Prog. Energy Combust. Sci. 84, 100901 (2021).

Article Google Scholar

Arshad, H., Sulaiman, S. A., Hussain, Z., Naz, M. Y. & Moni, M. N. Z. Effect of input power and process time on conversion of pure and mixed plastics into fuels through microwave-metal interaction pyrolysis. Waste Biomass Valorization 12(6), 3443–3457 (2021).

Article CAS Google Scholar

Suriapparao, D. V. & Vinu, R. Resource recovery from synthetic polymers via microwave pyrolysis using different susceptors. J. Anal. Appl. Pyrol. 113, 701–712 (2015).

Article CAS Google Scholar

Sonawane, Y. B., Shindikar, M. R. & Khaladkar, M. Y. High calorific value fuel from household plastic waste by catalytic pyrolysis. Nat. Environ. Pollut. Technol. 16(3), 879 (2017).

CAS Google Scholar

Muhyuddin, M., Mustarelli, P. & Santoro, C. Recent advances in waste plastic transformation into valuable platinum-group metal-free electrocatalysts for oxygen reduction reaction. Chemsuschem 14(18), 3785–3800 (2021).

Article CAS PubMed PubMed Central Google Scholar

Yao, L. et al. Microwave-assisted decomposition of waste plastic over Fe/FeAl2O4 to produce hydrogen and carbon nanotubes. J. Anal. Appl. Pyroly. 165, 105577 (2022).

Article CAS Google Scholar

Singh, R. K., Ruj, B., Sadhukhan, A. K. & Gupta, P. Thermal degradation of waste plastics under non-sweeping atmosphere: Part 1: Effect of temperature, product optimization, and degradation mechanism. J. Environ. Manage. 239, 395–406 (2019).

Article CAS PubMed Google Scholar

Saeaung, K., Phusunti, N., Phetwarotai, W., Assabumrungrat, S. & Cheirsilp, B. Catalytic pyrolysis of petroleum-based and biodegradable plastic waste to obtain high-value chemicals. Waste Manage. 127, 101–111 (2021).

Article CAS Google Scholar

Mousavi, S. A. H. S., Sadrameli, S. M. & Dehaghani, A. H. S. Energy recovery from high density polyethylene plastic via pyrolysis with upgrading of the product by a novel nano MIL-53 (Cu) derived@ Y zeolite catalyst using response surface methodology. Fuel Process. Technol. 231, 107257 (2022).

Article Google Scholar

Panda, A. K. Thermo-catalytic degradation of different plastics to drop in liquid fuel using calcium bentonite catalyst. Int. J. Ind. Chem. 9(2), 167–176 (2018).

Article CAS Google Scholar

Undri, A., Rosi, L., Frediani, M. & Frediani, P. Efficient disposal of waste polyolefins through microwave assisted pyrolysis. Fuel 116, 662–671 (2014).

Article CAS Google Scholar

Chen, W., Shi, S., Zhang, J., Chen, M. & Zhou, X. Co-pyrolysis of waste newspaper with high-density polyethylene: Synergistic effect and oil characterization. Energy Convers. Manage. 112, 41–48 (2016).

Article CAS Google Scholar

Bajad, G. S., Vijayakumar, R. P., Gupta, A. G., Jagtap, V. & Singh, Y. Production of liquid hydrocarbons, carbon nanotubes and hydrogen rich gases from waste plastic in a multi-core reactor. J. Anal. Appl. Pyrol. 125, 83–90 (2017).

Article CAS Google Scholar

Aboul-Enein, A. A., Arafa, E. I., Abdel-Azim, S. M. & Awadallah, A. E. Synthesis of multiwalled carbon nanotubes from polyethylene waste to enhance the rheological behavior of lubricating grease. Fuller. Nanotub. Carbon Nanostruct. 29(1), 46–57 (2021).

Article ADS CAS Google Scholar

Cai, N. et al. High-value products from ex-situ catalytic pyrolysis of polypropylene waste using iron-based catalysts: The influence of support materials. Waste Manag. 136, 47–56 (2021).

Article CAS PubMed Google Scholar

Veksha, A. et al. Processing of flexible plastic packaging waste into pyrolysis oil and multi-walled carbon nanotubes for electrocatalytic oxygen reduction. J. Hazard. Mater. 387, 121256–121316 (2020).

Article CAS PubMed Google Scholar

Liu, J., Jiang, Z., Yu, H. & Tang, T. Catalytic pyrolysis of polypropylene to synthesize carbon nanotubes and hydrogen through a two-stage process. Polym. Degrad. Stab. 96(10), 1711–1719 (2011).

Article CAS Google Scholar

Xu, G. et al. Self-perpetuating carbon foam microwave plasma conversion of hydrocarbon wastes into useful fuels and chemicals. Environ. Sci. Technol. 55(9), 6239–6247 (2021).

Article ADS CAS PubMed Google Scholar

Jiang, Z., Song, R., Bi, W., Lu, J. & Tang, T. Polypropylene as a carbon source for the synthesis of multi-walled carbon nanotubes via catalytic combustion. Carbon 45(2), 449–458 (2007).

Article CAS Google Scholar

Zhang, J., Du, J., Qian, Y. & Xiong, S. Synthesis, characterization and properties of carbon nanotubes microspheres from pyrolysis of polypropylene and maleated polypropylene. Mater. Res. Bull. 45(1), 15–20 (2010).

Article Google Scholar

Jesudoss, S. K. et al. Anti-cancer activity of hierarchical ZSM-5 zeolites synthesized from rice-based waste materials. RSC Adv. 8(1), 481–490 (2018).

Article ADS CAS Google Scholar

Cai, N. et al. Pyrolysis-catalysis of different waste plastics over Fe/Al2O3 catalyst: High-value hydrogen, liquid fuels, carbon nanotubes and possible reaction mechanisms. Energy Convers. Manage. 229, 113794 (2021).

Article CAS Google Scholar

Wang, J., Shen, B., Lan, M., Kang, D. & Wu, C. Carbon nanotubes (CNTs) production from catalytic pyrolysis of waste plastics: The influence of catalyst and reaction pressure. Catal. Today 351, 50–57 (2020).

Article CAS Google Scholar

Yousef, S., Eimontas, J., Zakarauskas, K. & Striūgas, N. A new sustainable strategy for oil, CH4 and aluminum recovery from metallised food packaging plastics waste using catalytic pyrolysis over ZSM-5 zeolite catalyst. Thermochim. Acta 713, 179223 (2022).

Article CAS Google Scholar

Hussein, Z. A., Shakor, Z. M., Alzuhairi, M. & Al-Sheikh, F. The yield of gasoline range hydrocarbons from plastic waste pyrolysis. Energy Sources, Part A Recovery Utilization Environ. Effects 44(1), 718–731 (2022).

Article CAS Google Scholar

Dierkes, G. et al. Quantification of microplastics in environmental samples via pressurized liquid extraction and pyrolysis-gas chromatography. Anal. Bioanal. Chem. 411(26), 6959–6968 (2019).

Article CAS PubMed Google Scholar

Botas, J. A., Serrano, D. P., García, A. & Ramos, R. Catalytic conversion of rapeseed oil for the production of raw chemicals, fuels and carbon nanotubes over Ni-modified nanocrystalline and hierarchical ZSM-5. Appl. Catal. B 145, 205–215 (2014).

Article CAS Google Scholar

Rahman, M. et al. Catalytic pyrolysis of single-use waste polyethylene for the production of liquid hydrocarbon using modified bentonite catalyst. Eur. J. Inorg. Chem. 2022(34), e202200409 (2022).

Article CAS Google Scholar

Madhu, P. et al. Production and characterization of maximum liquid oil products through individual and copyrolysis of pressed neem oil cake and waste thermocol mixture. Adv. Polym. Technol. 2022, 1–11 (2022).

Article Google Scholar

Download references

The authors acknowledge the support from the Deanship of Scientific Research, Najran University. Kingdom of Saudi Arabia, for funding this work under the National Research Priorities and Najran Area funding program grant code number (NU/NRP/SERC/12/2).

The APC of the journal was paid by Uniwersytet Rolniczy im. H. Kołł ˛ataja w Krakowie al. Mickiewicza 21, 31–120 Kraków, Poland (NIP 675 000 21 18).

Electrical Engineering Department, College of Engineering, Najran University Saudi Arabia, Najran, 61441, Saudi Arabia

Muhammad Irfan & Saifur Rahman

Department of Physics, University of Agriculture Faisalabad, Faisalabad, 38040, Pakistan

Rishmail Saleem, Bilal Shoukat, Shazia Shukrullah & Muhammad Yasin Naz

Department of Agricultural Engineering, Faculty of Agricultural Engineering & Technology, University of Agriculture Faisalabad, Faisalabad, 38040, Pakistan

Hammad Hussain

Civil Engineering Department, College of Engineering, Najran University, Najran, 61441, Saudi Arabia

Abdulnour Ali Jazem Ghanim

Department of Rural Building, Faculty of Environmental Engineering and Land Surveying, University of Agriculture in Krakow, Al. Mickiewicza 24/28, 30-059, Krakow, Poland

Grzegorz Nawalany

Department of Machine Operation, Ergonomics and Production Processes, Faculty of Production and Power Engineering, University of Agriculture in Krakow, 30-059, Krakow, Poland

Tomasz Jakubowski

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

Conceptualization, M.I.; Data curation, R.S.; Formal analysis, B.S. and H.H.; Funding acquisition, M.I.; Investigation, S.R., G.N. and T.J.; Methodology, B.S., H.H. and M.N.; Project administration, S.S.; Resources, A.G.; Validation, S.R.; Visualization, G.N.; Writing – original draft, R.S. and M.N.; Writing – review & editing, S.S., S.R. and T.J.

Correspondence to Shazia Shukrullah or Muhammad Yasin Naz.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Irfan, M., Saleem, R., Shoukat, B. et al. Production of combustible fuels and carbon nanotubes from plastic wastes using an in-situ catalytic microwave pyrolysis process. Sci Rep 13, 9057 (2023). https://doi.org/10.1038/s41598-023-36254-6

Download citation

Received: 29 January 2023

Accepted: 31 May 2023

Published: 03 June 2023

DOI: https://doi.org/10.1038/s41598-023-36254-6

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

SHARE